Aluminum row weight formula (kg) = 0.00271 × thickness × width × length
Aluminum weight formula (kg) = 0.00879 × wall thickness × (OD - Wall Thickness) × length
Aluminum weight formula (kg) = 0.00271 × thickness × width × length
Rod weight formula (kg) = 0.0022 × diameter × diameter × length(aluminum alloy )
Square rod weight formula (kg) = 0.0028 × edge width × width × length side
Square copper rod weight formula (kg) = 0.0089 × edge width × width × length side
Square brass rod weight formula (kg) = 0.0085 × edge width × width × length side
Aluminum checkered formula: weight per square meter thickness = 2.96 *(aluminum alloy 5052)
Haomei Aluminum has total annual production capacity of 200,000 metric ton aluminum sheet, strip and foil. It is equipped with 1+4 hot tandem rolling line, 4 cold mill production lines, and 5 foil mill production lines, and a complete complex of fishing equipment.welcome to order and visit our company!
Showing posts with label aluminum alloy 5052. Show all posts
Showing posts with label aluminum alloy 5052. Show all posts
Wednesday, 31 August 2016
solve the problem of aluminum alloy surface crack
Aluminum alloy flat ingot casting surface crack is a common defect.Aluminum alloy surface crack problems of semicontinuous casting process should consider many factors:
Mold taper;
Casting temperature '
Casting process slag
Melt Overheating;
Casting process too fast
cooling system
Alloy chemical composition
Skills
aluminum alloy 5052
Aluminum alloy flat ingot surface crack of solution:
The key to solve this problem to consider three main links:
Is the varieties of alloy chemical composition control
Varieties of casting process is alloy.
Is operation skills and natural conditions.
3003 h14 aluminum
The crystallization of aluminum alloy is also called the condensing tank, play a decisive role for casting.Aluminum alloy changes of taper of mould for casting can not be ignored.Taper of mould is too large flat ingot casting surface segregation tumors will increase, once the operation is not good will surface cracks, slag generated again when too narrow casting slab ingot mould can produce the surface cracking.A good teacher will adjust the size of the mould, casting to prevent flat bursts in the casting surface crack.
Aluminum alloy flat ingot surface crack for cooling water is very important.Cooling water is distributed evenly, bedding face and small surface strength, water size, water temperature are very big influence on solid-liquid region.
To sum up, the aluminum alloy flat ingot surface crack is made one of the common defects in the process of melting, eight analysis reason should be attention in the process of casting, will be the fault to ignore every detail, loss and waste.The control problem of alloy composition and impurities as well as the process setting need to be studied according to different environment analysis, make accurate judgment.For example: the surface of the aluminum alloy flat ingot slag smelting operation again in one of the most cause of surface crack.Majority is caused by improper operation, such as furnace temperature control - water - speed - flow disk horn mouth whether level off - crystallizer liquid surface height, there is every detail such as the operation.In order to prevent the happening of the aluminum alloy flat ingot surface crack phenomenon.From semi-continuous casting to the fully automatic casting, such as: automatic internal quality of casting defects is a new topic.For example: plume crystal column crystal. The vertical tree. Shining crystal column and prevention, such as we will continue to study and explore.
Mold taper;
Casting temperature '
Casting process slag
Melt Overheating;
Casting process too fast
cooling system
Alloy chemical composition
Skills
aluminum alloy 5052
Aluminum alloy flat ingot surface crack of solution:
The key to solve this problem to consider three main links:
Is the varieties of alloy chemical composition control
Varieties of casting process is alloy.
Is operation skills and natural conditions.
3003 h14 aluminum
The crystallization of aluminum alloy is also called the condensing tank, play a decisive role for casting.Aluminum alloy changes of taper of mould for casting can not be ignored.Taper of mould is too large flat ingot casting surface segregation tumors will increase, once the operation is not good will surface cracks, slag generated again when too narrow casting slab ingot mould can produce the surface cracking.A good teacher will adjust the size of the mould, casting to prevent flat bursts in the casting surface crack.
Aluminum alloy flat ingot surface crack for cooling water is very important.Cooling water is distributed evenly, bedding face and small surface strength, water size, water temperature are very big influence on solid-liquid region.
To sum up, the aluminum alloy flat ingot surface crack is made one of the common defects in the process of melting, eight analysis reason should be attention in the process of casting, will be the fault to ignore every detail, loss and waste.The control problem of alloy composition and impurities as well as the process setting need to be studied according to different environment analysis, make accurate judgment.For example: the surface of the aluminum alloy flat ingot slag smelting operation again in one of the most cause of surface crack.Majority is caused by improper operation, such as furnace temperature control - water - speed - flow disk horn mouth whether level off - crystallizer liquid surface height, there is every detail such as the operation.In order to prevent the happening of the aluminum alloy flat ingot surface crack phenomenon.From semi-continuous casting to the fully automatic casting, such as: automatic internal quality of casting defects is a new topic.For example: plume crystal column crystal. The vertical tree. Shining crystal column and prevention, such as we will continue to study and explore.
Monday, 1 August 2016
solve the problem of aluminum alloy surface crack
Aluminum alloy flat ingot casting surface crack is a common defect.Aluminum alloy surface crack problems of semicontinuous casting process should consider many factors:
Mold taper;
Casting temperature '
Casting process slag
Melt Overheating;
Casting process too fast
cooling system
Alloy chemical composition
Skills
aluminum alloy 5052
Aluminum alloy flat ingot surface crack of solution:
The key to solve this problem to consider three main links:
Is the varieties of alloy chemical composition control
Varieties of casting process is alloy.
Is operation skills and natural conditions.
3003 h14 aluminum
The crystallization of aluminum alloy is also called the condensing tank, play a decisive role for casting.Aluminum alloy changes of taper of mould for casting can not be ignored.Taper of mould is too large flat ingot casting surface segregation tumors will increase, once the operation is not good will surface cracks, slag generated again when too narrow casting slab ingot mould can produce the surface cracking.A good teacher will adjust the size of the mould, casting to prevent flat bursts in the casting surface crack.
Aluminum alloy flat ingot surface crack for cooling water is very important.Cooling water is distributed evenly, bedding face and small surface strength, water size, water temperature are very big influence on solid-liquid region.
To sum up, the aluminum alloy flat ingot surface crack is made one of the common defects in the process of melting, eight analysis reason should be attention in the process of casting, will be the fault to ignore every detail, loss and waste.The control problem of alloy composition and impurities as well as the process setting need to be studied according to different environment analysis, make accurate judgment.For example: the surface of the aluminum alloy flat ingot slag smelting operation again in one of the most cause of surface crack.Majority is caused by improper operation, such as furnace temperature control - water - speed - flow disk horn mouth whether level off - crystallizer liquid surface height, there is every detail such as the operation.In order to prevent the happening of the aluminum alloy flat ingot surface crack phenomenon.From semi-continuous casting to the fully automatic casting, such as: automatic internal quality of casting defects is a new topic.For example: plume crystal column crystal. The vertical tree. Shining crystal column and prevention, such as we will continue to study and explore.
Mold taper;
Casting temperature '
Casting process slag
Melt Overheating;
Casting process too fast
cooling system
Alloy chemical composition
Skills
aluminum alloy 5052
Aluminum alloy flat ingot surface crack of solution:
The key to solve this problem to consider three main links:
Is the varieties of alloy chemical composition control
Varieties of casting process is alloy.
Is operation skills and natural conditions.
3003 h14 aluminum
The crystallization of aluminum alloy is also called the condensing tank, play a decisive role for casting.Aluminum alloy changes of taper of mould for casting can not be ignored.Taper of mould is too large flat ingot casting surface segregation tumors will increase, once the operation is not good will surface cracks, slag generated again when too narrow casting slab ingot mould can produce the surface cracking.A good teacher will adjust the size of the mould, casting to prevent flat bursts in the casting surface crack.
Aluminum alloy flat ingot surface crack for cooling water is very important.Cooling water is distributed evenly, bedding face and small surface strength, water size, water temperature are very big influence on solid-liquid region.
To sum up, the aluminum alloy flat ingot surface crack is made one of the common defects in the process of melting, eight analysis reason should be attention in the process of casting, will be the fault to ignore every detail, loss and waste.The control problem of alloy composition and impurities as well as the process setting need to be studied according to different environment analysis, make accurate judgment.For example: the surface of the aluminum alloy flat ingot slag smelting operation again in one of the most cause of surface crack.Majority is caused by improper operation, such as furnace temperature control - water - speed - flow disk horn mouth whether level off - crystallizer liquid surface height, there is every detail such as the operation.In order to prevent the happening of the aluminum alloy flat ingot surface crack phenomenon.From semi-continuous casting to the fully automatic casting, such as: automatic internal quality of casting defects is a new topic.For example: plume crystal column crystal. The vertical tree. Shining crystal column and prevention, such as we will continue to study and explore.
Tuesday, 19 July 2016
Aluminum factory supply aluminum plate, Haomei aluminum
Haomei aluminum, we have large of high-quality 1060 pure aluminum, aluminum coil, aluminum foil, aluminum alloy, aluminum mirror, brushed aluminum oxide, cheap, puerile.
1050 food, chemical and brewing industry extrusion coil, various hoses, fireworks powder
1060 corrosion resistance and formability requirements are high occasion, but ask for strength, chemical equipment is its typical use
1100 for processing need to have good formability and high corrosion resistance but do not require high strength parts and components, such as chemical products, food industry equipment and storage containers, sheet metal parts, deep drawing or spinning hollowware, welding parts, heat exchangers, printing plates, nameplates, reflective devices
3003 for processing need to have good formability, high corrosion resistance weldability good parts components, or both of these performance requirements and the need to have a high ratio 1XXX alloy strength work, such as kitchen utensils, food and chemical products processing and storage devices, transport liquid product tank, tank to sheet metal processing various pressure vessels and piping
3004 aluminum cans cans, requiring a higher strength than the 3003 alloy parts, chemical products and storage equipment, sheet metal parts, construction machined parts, construction tools, a variety of lighting components
3105 room partition, baffle, activities room board, gutters and downspouts, sheet forming machining parts, bottle caps, corks, etc.
5005 and 3003 aluminium alloy similar, with moderate strength and good corrosion resistance. Used as a conductor, cookware, dashboard, shell and architectural decoration pieces. Anodized film brighter than the oxide film on the 3003 alloy and 6063 alloy with coordinated colors
5050 aluminium sheet as cooler and refrigerator liner board, car trachea, tubing and agricultural irrigation pipe; also can be processed plate, pipe, bar, contoured wood and wire, etc.
5052 aluminium alloy has good forming properties, corrosion resistance, can be candles, fatigue strength and static strength medium, for the manufacture of aircraft fuel tanks, fuel lines, and transportation vehicles, ship sheet metal parts, instruments, lights bracket and rivets , metal products
5056 magnesium alloy and cable sheathing rivets, zippers, nails, etc; clad aluminum wire is widely used in the processing of agricultural insect traps cover, and the need for high corrosion resistance of other occasions
5083 for applications that require high corrosion resistance, good weldability and moderate-intensity occasions, such as ships, cars and airplanes plate weldment; should be strictly fireproof pressure vessels, refrigeration equipment, tower, drilling equipment, transportation transportation equipment, missile components, armor, etc.
5086 for applications that require high corrosion resistance, good weldability and moderate-intensity occasions, such as ships, automobiles, aircraft, cryogenic equipment, tower, drilling equipment, transportation equipment, missile parts and deck, etc.
7005 extruded material for the manufacture of both a high strength but also have high fracture toughness of welded structures, such as transportation vehicles truss rod member, the container; large heat exchangers, and a solid solution can not be processed after welding components; also used in the manufacture of sports equipment such as tennis rackets and baseball bats
7050 aircraft structural parts with plate, extrusions, forgings and die forgings. Manufacture of such parts of the alloy requirements are: anti-spalling corrosion, stress corrosion cracking, fracture toughness and fatigue performance are high
7075 for the manufacture of aircraft structures and Futures He demanded a high strength, corrosion resistance and strong high-stress structural parts, mold manufacturing
1050 food, chemical and brewing industry extrusion coil, various hoses, fireworks powder
1060 corrosion resistance and formability requirements are high occasion, but ask for strength, chemical equipment is its typical use
1100 for processing need to have good formability and high corrosion resistance but do not require high strength parts and components, such as chemical products, food industry equipment and storage containers, sheet metal parts, deep drawing or spinning hollowware, welding parts, heat exchangers, printing plates, nameplates, reflective devices
3003 for processing need to have good formability, high corrosion resistance weldability good parts components, or both of these performance requirements and the need to have a high ratio 1XXX alloy strength work, such as kitchen utensils, food and chemical products processing and storage devices, transport liquid product tank, tank to sheet metal processing various pressure vessels and piping
3004 aluminum cans cans, requiring a higher strength than the 3003 alloy parts, chemical products and storage equipment, sheet metal parts, construction machined parts, construction tools, a variety of lighting components
3105 room partition, baffle, activities room board, gutters and downspouts, sheet forming machining parts, bottle caps, corks, etc.
5005 and 3003 aluminium alloy similar, with moderate strength and good corrosion resistance. Used as a conductor, cookware, dashboard, shell and architectural decoration pieces. Anodized film brighter than the oxide film on the 3003 alloy and 6063 alloy with coordinated colors
5050 aluminium sheet as cooler and refrigerator liner board, car trachea, tubing and agricultural irrigation pipe; also can be processed plate, pipe, bar, contoured wood and wire, etc.
5052 aluminium alloy has good forming properties, corrosion resistance, can be candles, fatigue strength and static strength medium, for the manufacture of aircraft fuel tanks, fuel lines, and transportation vehicles, ship sheet metal parts, instruments, lights bracket and rivets , metal products
5056 magnesium alloy and cable sheathing rivets, zippers, nails, etc; clad aluminum wire is widely used in the processing of agricultural insect traps cover, and the need for high corrosion resistance of other occasions
5083 for applications that require high corrosion resistance, good weldability and moderate-intensity occasions, such as ships, cars and airplanes plate weldment; should be strictly fireproof pressure vessels, refrigeration equipment, tower, drilling equipment, transportation transportation equipment, missile components, armor, etc.
5086 for applications that require high corrosion resistance, good weldability and moderate-intensity occasions, such as ships, automobiles, aircraft, cryogenic equipment, tower, drilling equipment, transportation equipment, missile parts and deck, etc.
7005 extruded material for the manufacture of both a high strength but also have high fracture toughness of welded structures, such as transportation vehicles truss rod member, the container; large heat exchangers, and a solid solution can not be processed after welding components; also used in the manufacture of sports equipment such as tennis rackets and baseball bats
7050 aircraft structural parts with plate, extrusions, forgings and die forgings. Manufacture of such parts of the alloy requirements are: anti-spalling corrosion, stress corrosion cracking, fracture toughness and fatigue performance are high
7075 for the manufacture of aircraft structures and Futures He demanded a high strength, corrosion resistance and strong high-stress structural parts, mold manufacturing